LGGB 2 is a biodegradable, low toxicity grease, synthetic ester oil based using a lithium-calcium thickener. It has excellent lubrication properties for a wide range of applications operating under different conditions.
- Compliance with current regulations on toxicity and biodegradability
- Good performance in applications with steel-on-steel spherical plain bearings, ball bearings and roller bearings
- Good low temperature start-up performance
- Good corrosion inhibiting properties
- Suitable for medium to high loads
|
Features:
LGGB 2 is a biodegradable, low toxicity grease, synthetic ester oil based using a lithium-calcium thickener. It has excellent lubrication properties for a wide range of applications operating under different conditions.
This grease offers:
- Compliance with current regulations on toxicity and biodegradability
- Good performance in applications with steel-on-steel spherical plain bearings, ball bearings and roller bearings
- Good low temperature start-up performance
- Good corrosion inhibiting properties
- Suitable for medium to high loads
Available pack sizes
- SYSTEM 24
- 420 ml cartridge
- 5 kg can
- 18 kg can
- 180 kg drum
Technical data
- DIN 51825 code : KPE 2K-40
- NLGI consistency class : 2
- Soap type : lithium / calcium
- Colour : off white Base oil type : synthetic ester
- Operating temperature range, ºC (ºF) : -40 to 120 (-40 to 250)
- Dropping point DIN ISO 2176, ºC (ºF) : >170 (>338)
- Base oil viscosity 40 ºC, mm2/s : 110 100 ºC,mm2/s : 13
- Penetration DIN ISO 2137
- 60 strokes, 10-1 mm : 265-295
- 100,000 strokes, 10-1 mm : <30
- Mechanical stability
- Roll stability, 50 hours at 80 ºC, change 10-1 mm : +50 max. change
- Roll stability, 72 hours at 100 ºC, change 10-1 mm : -
- SKF V2F test : -
- Corrosion protection SKF Emcor:
- standard ISO 11007 : 0 - 0
- water washout test : -
- salt water test (100% seawater) : -
- Water resistance
- DIN 51 807/1, 3 hrs at 90 ºC : 1 max.
- Oil separation
- DIN 51 817, 7 days at 40 ºC, static, % : 1 - 2
- Lubricating ability
- SKF R2F, running test B : pass at 100 °C (212 °F)
- Copper corrosion
- Rolling bearing grease life
- SKF R0F test L50 life at 10 000 rpm, hrs : >500 at 120 °C (250 °F)
- EP performance
- Wear scar, DIN 51350/5, 1400 N, mm : 1,68
- 4 ball test, welding load, DIN 51350/4 : 2500 N
- Designation : LGGB 2/(pack size)
|
|