LGET 2 is a premium quality, synthetic fluorinated oil based grease using a PTFE thickener. It has excellent lubrication properties at extremely high temperatures exceeding 200 ºC (392 ºF) up to 260 ºC (500 ºF).

This grease offers:

• Long life in aggressive environments such as very reactive environments or areas with a presence of high purity gaseous oxygen, hexane and so on
• Excellent oxidation resistance
• Good corrosion resistance
• Excellent water and steam resistance

Available pack sizes

• 50 g (25 ml) syringe
• 1 kg can

Technical data

• DIN 51825 code : KFK2U-40
• NLGI consistency class : 2
• Soap type : PTFE
• Colour : whitish cream
• Base oil type : synthetic (fluorinated polyether)
• Operating temperature range, ºC (ºF) : -40 to 260 (-40 to 500)
• Dropping point DIN ISO 2176, ºC (ºF) : >300 (572)
• Base oil viscosity
  • 40 ºC, mm2/s : 400
  • 100 ºC,mm2/s : 38
• Penetration DIN ISO 2137
  • 60 strokes, 10-1 mm : 265-295
  • 100,000 strokes, 10-1 mm : -
• Mechanical stability
  • Roll stability, 50 hours at 80 ºC, change 10-1 mm : ±30 max. (130 °C/266 °F)
  • Roll stability, 72 hours at 100 ºC, change 10-1 mm : -
  • SKF V2F test : -
• Corrosion protection SKF Emcor:
  • standard ISO 11007 : 0 - 1
  • water washout test : -
  • salt water test (100% seawater) : -
• Water resistance
  • DIN 51 807/1, 3 hrs at 90 ºC : 1 max.
• Oil separation
  • DIN 51 817, 7 days at 40 ºC, static, % : 2 - 3
• Lubricating ability
  • SKF R2F, running test B : -
• Copper corrosion
  • DIN 51 811, 100 °C : 1 (150 °C/300 °F)
• Rolling bearing grease life
  • SKF R0F test L50 life at 10 000 rpm, hrs : >700, 5600 rpm at 220 °C (428 °F)
• EP performance
  • Wear scar, DIN 51350/5, 1400 N, mm : -
  • 4 ball test, welding load, DIN 51350/4 : 4000 min.
• Designation : LGET 2/0.05

Important note:
Fluorinated greases in general are very costly, however LGET 2 is competitively priced. Given that LGET 2 is more expensive than other SKF greases, it is therefore recommended to use it only for applications where other SKF greases would not provide the required performance.