LGHP 2 is a premium quality grease, mineral oil based using Polyurea (di-urea) thickener. It has excellent lubrication properties for a wide temperature range from -40 °C (-40 °F) up to 150 °C (302 °F).

This grease replaces the SKF high temperature grease LGHQ 3

This grease offers:

• Extremely long life at high temperature
• Wide temperature range
• Excellent corrosion protection
• High thermal stability
• Good low temperature start-up performance
• Compatibility with common Polyurea greases
• Compatibility with lithium complex thickened greases

Available pack sizes

• 420 ml cartridge
• 1 kg can
• 5 kg can
• 18 kg can
• 180 kg drum

Technical data

• DIN 51825 code : K2N-40
• NLGI consistency class : 2 - 3
• Soap type : di-urea
• Color : blue
• Base oil type : mineral
• Operating temperature range, ºC (ºF) : -40 to 150 (-40 to 300)
• Dropping point DIN ISO 2176, ºC (ºF) : 240 min. (464 min.)
• Base oil viscosity 40 ºC, mm2/s : 96 100 ºC,mm2/s : 10,5
• Penetration DIN ISO 2137
  • 60 strokes, 10-1 mm : 245-275
  • 100,000 strokes, 10-1 mm : 365 max.
• Mechanical stability
  • Roll stability, 50 hours at 80 ºC, change 10-1 mm : 365 max.
  • SKF V2F test : -
• Corrosion protection - SKF Emcor:
  • standard ISO 11007 : 0 - 0
  • water washout test : 0 - 0
  • salt water test (100% seawater) : 0 - 0
• Water resistance
  • DIN 51 807/1, 3 hrs at 90 ºC : 1 max.
• Oil separation
  • DIN 51 817, 7 days at 40 ºC, static, % : 0,7 - 3
• Lubricating ability
  • SKF R2F, running test B at 120 °C : pass
• Copper corrosion
  • DIN 51 811, 100 °C : 1 max. (150 °C/300 °F)
• Rolling bearing grease life
  • SKF R0F test L50 life at 10 000 rpm, hrs : 1000 min. at 150 °C (302 °F)
• EP performance
  • Wear scar, DIN 51350/5, 1400 N, mm : -
  • 4 ball test, welding load, DIN 51350/4 : -
• Designation : LGHP 2/(pack size)