LGWA 2 is a premium quality mineral oil based lithium complex grease. LGWA 2 has such properties that it can be recommended for a wide range of industrial and automotive applications.
This grease offers:
- Excellent lubrication at peak temperatures up to 220 °C (428 °F) for short periods
- Protection of wheel bearings operating under severe conditions
- Effective lubrication in wet conditions
- Good water and corrosion resistance
- Excellent lubrication under high loads and low speeds
Available pack sizes
- SYSTEM 24
- 35 g tube
- 200 g tube
- 420 ml cartridge
- 1 kg can
- 5 kg can
- 50 kg drum
- 180 kg drum
Technical data
- DIN 51825 code : K2N-30
- NLGI consistency class : 2
- Soap type : lithium complex
- Colour : amber
- Base oil type : mineral
- Operating temperature range, ºC (ºF) : -30 to 140 (-22 to 284)
- Dropping point DIN ISO 2176, ºC (ºF) : >250 (482)
- Base oil viscosity
- 40 ºC, mm2/s : 185
- 100 ºC,mm2/s : 15
- Penetration DIN ISO 2137
- 60 strokes, 10-1 mm : 265-295
- 100,000 strokes, 10-1 mm : +50 max. (325 max.)
- Mechanical stability
- Roll stability, 50 hours at 80 ºC, change 10-1 mm : +50 max. change
- Roll stability, 72 hours at 100 ºC, change 10-1 mm : -
- SKF V2F test : 'M'
- Corrosion protection SKF Emcor:
- standard ISO 11007 : 0 - 0
- water washout test : 0 - 0
- salt water test (100% seawater) : -
- Water resistance
- DIN 51 807/1, 3 hrs at 90 ºC : 1 max.
- Oil separation
- DIN 51 817, 7 days at 40 ºC, static, % : 1 - 5
- Lubricating ability
- SKF R2F, running test B : pass at 100 °C (212 °F)
- Copper corrosion
- DIN 51 811, 100 °C : 2 max. (110 °C/230 °F)
- Rolling bearing grease life
- SKF R0F test L50 life at 10 000 rpm, hrs : -
- EP performance
- Wear scar, DIN 51350/5, 1400 N, mm : 1,6 max.
- 4 ball test, welding load, DIN 51350/4 : 2600 min.
- Designation : LGWA 2/(pack size)
|